1 Experimental Background

Resin lotion is widely used in coatings, adhesives, textiles and other fields. The purpose of this experiment is to achieve high-pressure homogenizationGSL-100Process, optimize the particle size distribution of the resin lotion with a specific formula, and observe whether it is stratified.

High pressure homogenizer GSL-100

II Experimental Procedure

1.Sample preparation: take the sample (treated with a magnetic stirrer) and the original lotion of the resin is slightly milky white in appearance.

2.Parameter setting: Install the high-pressure homogenizerGSL-100Perform cleaning and preheating30Degree. Set the homogenization pressure to20-40 -50MPa. proceed3A loop processing.

3.Homogenization treatment: click Start, the lotion passes through the homogenization valve under high pressure, completes the set cycle times, and collects the homogenized samples.

4.Performance observation: immediately compare the samples before and after treatment: after homogenization, the lotion appears uniform without layering, standing30After minutes, no significant stratification was observed.

III Experimental Summary

In this experiment, high pressure homogenizer was successfully used to homogenize the resin lotion. The experimental results indicate that:

1.The processed sample has a uniform and delicate texture, indicating a significant improvement in dispersibility.

2.There is no stratification in the short-term standing, indicating that the homogenization treatment effectively reduces the settling rate of particles and enhances the physical stability of lotion.

4、 Experimental comparison chart